Chemical Composition
Chemical Components

Austenitic Types

For general information only, contact factory for availability.

Type
C
Max.
Mn
Max.
P
Max.
S
Max.
Si
Max.
Cr
Ni
Mo
Max.
Other
Elements
201
202
301
302
303
0.15
0.15
0.15
0.15
0.15
5.50-7.50
7.50-10.00
2.00
2.00
2.00
.060
.060
.045
.045
.20
.030
.030
.030
.030
.15 Min.
1.00
1.00
1.00
1.00
1.00
16.00-16.00
17.00-19.00
16.00-15.00
17.00-19.00
17.00-19.00
3.50-5.50
4.00-6.00
6.00-6.00
5.00-10.00
8.00-10.00
-
-
-
-
-
N 0.25 Max
N 0.25 Max
-
-
-
30356
304
304L
305
308
0.15
0.08
0.03
0.12
0.08
2.00
2.00
2.00
2.00
2.00
.20
.045
.045
.045
.045
.060
.030
.030
.030
.030
1.00
1.00
1.00
1.00
1.00
17.00-19.00
18.00-20.00
18.00-20.00
17.00-19.00
19.00-21.00
8.00-10.00
8.00-10.00
8.00-10.00
10.50-13.00
10110-12.00
-
-
-
-
-
Se 0.15 Min
-
-
-
-
309
3095
310
3105
314
0.20
0.08
0.25
0.08
0.25
2.00
2.00
2.00
2.00
2.00
.045
.045
.045
.045
.045
.030
.030
.030
.030
.030
1.00
1.00
1.50
1.50
1.50-3.00
22.00-24.00
22.00-24.00
24.00-26.00
24.00-26.00
23.00-26.00
12.00-15.00
12.00-15.00
19.00-22.00
19.00-22.00
19.00-22.00
-
-
-
-
-
-
-
-
-
-
316
316L
316F
317
317L
0.08
0.03
0.08
0.08
0.03
2.00
2.00
2.00
2.00
2.00
.045
.045
.20
.045
.045
.030
.030
.10 mm
.030
.030
1.00
1.00
1.00
1.00
1.00
16.00-18.00
16.00-18.00
16.00-18.00
18.00-20.00
18.00-20.00
10.00-14.00
10.00-14.00
10.00-14.00
11.00-15.00
11.00-15.00
2.00-3.00
2.00-3.00
1.75-3.00
3.00-4.00
3.00-4.00
-
-
-
-
-
321
330
347


348
0.08
0.20
0.02


0.08
2.00
2.00
2.00


2.00
.045
.03
.045


.045
.030
.030
.030


.030
1.00
.75-1.50
1.00


1.00
17.00-19.00
17.00-20.00
17.00-19.00


17.00-19.00
9.00-12.00
34.00-37.00
9.00-13.00


9.00-13.00
-
-
-
-
-
-
Ti SaC Mm

Cb-Ta 10 x
C Mm
Cb-Ta 10 x
Mii.
384



0.08



2.00



.045



.030



1.00



15.00-17.00



17.00-19.00




Ta .10 Max
Co .20 Max

Cb + Ta 8
18-9L W
Nitronic 32
Nitronic 33
Nitronic 40
Nitronicso

0.10
0.15
0.08
0.08
.03-06

2.00
11.00-14.00
11.50-14.50
8.00-10.00
4.00-6.00

.045
.060
.060
.060
.040

.030
.030
.030
.030
.030

1.00
1.00
1.00
1.00
1.00

17.00-19.00
16.50-19.00
17.00-19.00
19.00-21.00
20.50-23.50

8.00-10.00
.50-2.50
2.25-3.75
5.50-7.50
11.50-13.50





1.50-3.00

Ba C Mm
Cu3 .0-40
N .20-45
N .20.40
N .15-40
N .20-40
Nitronic 60


0.10


7.00-9.00




3.50-4.50


16.00-18.00


8.00-9.00


-


Co .10-30
V .10-30
N .08-18

Hardenable (By Heat Treatment) Types

410
416
.150
.150
1.00
1.25
.040
.060
.030
.14 Mm.
1.00
1.00
11.50-13.50
12.00-14.00
-
-
-
-
-
-
420
17-4P6
.150 Mm.
.070
1.00
1.00
.040
.040
.030
.030
1.00
1.00
12.00-14.00
15.50-17.50
3.00-5.00

-
-
-
-
17-7PH
.090
1.00
.040
.030
1.00
16.00-18.00
6.50-7.75
-
-

Non-Hardenable Types

409
430
0.08
1.00
.045
.045
1.00
10.50-11.75
-
Ti 6 a C Mm.
0.12
1.00
.040
.030
1.00
16.00-18.00
-


Nominal Chemical Composition Nickel Alloys
Nickel Alloys
Type
Ni
C
Mn
Fe
S
Si
Cu
Cr
Al
Ti
Mg
Cb
Mo
Others
200
201
205
99.5
99.5
99.5
.080
.010
.080
.180
.180
.180
.20
.20
.10
.005
.005
.004
.180
.130
.080
.130
.130
.080
-
-
-
-
-
-
-
-
.030

.050

-
-
-
-
-
-
-
-
-
211
212
220
230
95.0
97.0
99.5
99.5
.100
.200
.040
.050
4.75
2.00
.100
.080
.380
.750
.050
.050
.008
.015
.004
.004
.080
.150
.030
.020
.130
.20
.050
.050
-
-
-
-
-
-
-
-
-
-
.030
.003
-
-
.050
.060
-
-
-
-
-
-
-
-
-
-
-
-
Monel (Nickel-Copper) Alloys.
400
66.s
0.15
1.00 1.25 0.012 0.25
31.5
-
Incoloy (Nickel-Chromium) Alloys
600
601
625
X-750
751


76.0
60.5
61.0
73.0
72.5


0.08
0.05
0.05
0.04
0.05


0.5
0.5
0.25
0.5
0.5


8
14.1
2.5
7
7


0.008
0.007
0.008
0.005
0.005


0.25
0.25
0.25
0.25
0.25


0.25
0.5
-
0.25
0.25


15.5
23
21.5
15.5
15.5


-
1.35
0.2
0.7
1.2


-
-
0.2
2.5
2.3


-
-
-
-



-
-
Ta
3.65
Ta
0.95
Ta 0.95
-
-
9
-
-


-
-
-

-


Incoloy (Nickel-Iron-Chromium) Alloys
800
801
802
32.5
32.0
32.5
0.05
0.05
0.35
0.75
0.75
0.75
46
44.5
46
0.008
0.008
0.008
0.5
0.5
0.38
0.38
0.25
-
21
20.5
21
0.38
-
0.58
0.38
1.13
0.75
-
-
-
-
-
-
-
-
-
-
-
-
804
805
41.0
36.0
0.05
0.12
0.75
0.75
25.4
Sal.
0.008
0.02
0.38
0.5
0.38
0.5
29.5
7.5
0.3
-
0.6
-
-
-
-
-

0.50
-
-